Plasma Niobium Surface Alloying of Pure Titanium and its Oxidation at 900 ℃

A niobium-modified layer on pure titanium surface was obtained by means of double glow plasma surface alloying technique. The modified layer was uniform, continuous, compact and well adhered to the substrate. The niobium composition in the modified layer decreased gradually from the surface to the substrate. The oxidation behavior of the niobium-modified layer was investigated and compared with the untreated surface at 900 ℃ for 100 h. Characterization of the layers was performed using X-ray diffraction and scanning electron microscope, respectively. The test results show that the oxidation behavior of pure titanium was improved by niobium alloying process. Niobium has a positive influence on the oxidation resistance.

作 者： WANG Wen-bo ZHONG Xu HE Zhi-yong WANG Zhen-xia ZHANG Ping-ze   作者單位： WANG Wen-bo,HE Zhi-yong,WANG Zhen-xia(Research Institute of Surface Engineering, Taiyuan University of Technology, Taiyuan 030024, China)

ZHONG Xu,ZHANG Ping-ze(Research Institute of Surface Engineering, Taiyuan University of Technology, Taiyuan 030024, China;Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China) 

刊 名： 中國航空學報(英文版)  ISTIC 英文刊名： CHINESE JOURNAL OF AERONAUTICS  年，卷(期)： 2007 20(2)  分類號： V2  關鍵詞： niobium   pure titanium   plasma surface alloying   oxidation  

【Plasma Niobium Surface Alloying of P】相關文章：

論可以P與可以不P的關系04-27

學科術語 P05-04

Lead adsorption capacities of different components in natural surface coatings04-26

Changes of plasma membrane ATPase activity,membrane potential and transmembrane proton gradient in Kandelia candel and A04-25

p2p業務員工作計劃01-07

p2p理財培訓心得體會05-17

神奇的Surface-pen-寫物作文600字04-24

LALA的美容心得貼P573-P577(8.2+)04-25

p2p理財培訓心得體會6篇05-17

Assessment of Cu, Pb and Hg Contamination in Bottom Sediments Of Surface Water in XuZhou04-26